Fumed Silica, Nanometer Silica

Fumed Silica, Nanometer Silica

 

The fumed silica has small size, large surface area, many of surface silicon alcohol based (Si-OH) , and body three-dimensional branch structure, through the hydrogen bonding or van der Waals force makes silica and polymer molecules and silica between the molecules which generate strong function, achieve reinforcing effect.

It has chemical inert and special thixotropic performance obviously improved rubber products tensile strength, tensile resistance and wear resistance, rubber increase strength several times after modified. Liquid system, adhesives, such as polymer rheology and thixotropy control, used as the sink, thickening, flow-linked fertilizer, HCR and RTV -2 K silicone rubber reinforcement, can be used to adjust the free flow and as an anticaking agent to improve powder properties and so on.

 

The technique index are described below:

 

XH-150

                    MODEL

ITEM

XH-105

Inspection Methods

Specific surface area (BET)(/g)

150±25

GB/T10722

Suspension PH value (4%)

3.74.5

GB/T1717

Loss on dying (dried at 105 for 2 hours)

≤1.5

GB/T5211.3

Loss on ignition (dried at 1000 for 2 hours , on dry basis)

≤2.0

GB/T20020

Screen tailings (45um)(m/m%)

≤0.04

GB/T5211.14

Filling density (on dry basis) (g/L)

4060

GB/T5211.14

Assay % as SiO2 (on ignition basis) (m/m%)

≥99.8

GB/T20020

Assay % as C (on dry basis) (m/m%)

≤0.15

GB/T20020

 

XH-200

                    MODEL

ITEM

XH-105

Inspection Methods

Specific surface area (BET)(/g)

200±25

Q/(GZ)GBS0

1-2002

Suspension PH value (4%)

3.64.5

ISO787-9

Loss on dying (dried at 105 for 2 hours)

≤1.5

ISO787-2

Loss on ignition (dried at 1000 for 2 hours , on dry basis)

≤2.5

ISO3262-1

Screen tailings (45um)(m/m%)

≤0.05

ISO787-18

Apparent density (g/L)

2560

ISO787-11

Assay % as SiO2 (on ignition basis) (m/m%)

≥99.9

ISO3262-20

Assay % as C (on dry basis) (m/m%)

≤0.2

ISO3262-20

Assay % as FeO2 (on dry basis) (m/m%)

≤0.003

ISO3262-20

Assay % as AlO2 (on dry basis) (m/m%)

≤0.05

ISO3262-20

Assay % as TiO2 (on dry basis) (m/m%)

≤0.03

ISO3262-20

 

Nanometer-Silica  XH-201

                    MODEL

ITEM

XH-201

Mesh

2000-2500

Appearance

White powder

Specific surface area (/g)

205-220

Assay % as SiO2  (on dry basis) (m/m%)

≥98.0

Loss on dying (dried at 105 for 2 hours)

5.0-6.0

Loss on ignition (dried at 1000 for 2 hours , on dry basis)

4.2-4.8

DBP Oil Absorption

2.30-2.70

PH value 10% suspending solution

6.6-7.1

Average particle size

4-11

Screen tailings (45um)(m/m%)

≤0.05

Total Fe %

≤0.025

Total Cu %

≤0.003

Total Mn %

≤0.005

Al2O3

≤0.020

MgO (%)

≤0.010

Na2SO4

≤0.5

CaO (%)

≤0.010

Whiteness %

≥98